Andy R Senior Retro Guru Feedback View Apr 17, 2009 #41 silverclaws":3uaujuf4 said: Yes, using brazing is probably safer than weld, less chance of burning holes through the thin metal, but what has to be remembered, is what you are actually doing when heating the frame to a temperature that will melt bronze. Click to expand... Silver solder is the best option if you want to go down this route - depending on the alloy it'll flow at around 400 Celsius. Small dents I wouldn't bother with though, and you couldn't use this method for large dents.......
silverclaws":3uaujuf4 said: Yes, using brazing is probably safer than weld, less chance of burning holes through the thin metal, but what has to be remembered, is what you are actually doing when heating the frame to a temperature that will melt bronze. Click to expand... Silver solder is the best option if you want to go down this route - depending on the alloy it'll flow at around 400 Celsius. Small dents I wouldn't bother with though, and you couldn't use this method for large dents.......