jimo746":1tw3apdy said:Ally suffers from galling more.
Ti is prone to a chemical reaction with dissimilar metals which can result in the two parts literally "weld" themselves together, not good when you're talking about an expensive Ti frame & components.
Plenty of suitable lube/anti-seize and perhaps more regular maintainance and all should be well.
I've not had a Ti frame before, but have had Ti components/bolts etc and after using "Ti-Prep" or Copper grease have never had any issues.
's what I heard and also that the copper in copper grease can react with metals so a plain old vanila grease should better.